Multilayer Zirconia
- Fitur
- barang-barang tambahan
- tech Specs
- Émbaran pamundut
Features of Multilayer Zirconia
The multilayer zirconia has better shade gradation and more natural on aesthetics with translucency in the incisal area and bending strength for anterior and posterior teeth restorations with up to full arch bridges.
-
Konsisten VITA® Klasik Shade Cocog
Tuturkeun sacara ketat VITA® Classic Shade tina fase R&D sareng ogé ku produksi standar sareng pertandingan shade.
-
Glazed with Bloomden CeramStar Glaze/Stain Kit
Preparation: Multilayer crown bridge after milled and sintered and then glazed.
-
Shade gradation more natural
Compared preshaded zirconia, the multilayer zirconia has better shade gradation because of its powder gradiaent to make various shade layers.
-
STML for Full arch bridges
STML is with highest bending strength 1100MPa for bridges and even long-span curved cases or full arch bridges by the lab-test.
Accessories for Multilayer Zirconia
-
KeramikStar® Glaze / kokotor Gingival Setel
Éta ngandung 4 massa tunggal ogé cairan khusus sareng asesoris. Pasta 3D dikembangkeun khusus pikeun finalisasi éstétika sareng karakterisasi bagian warna gingival tina restorasi keramik, didamel tina litium disilicate sareng 3D Pro Multilayer. Sadaya bagian tina set ogé sayogi masing-masing.
DIAJAR DEUI -
KeramikStar® Glaze / Stain Vivid Set
Éta ngandung 7 massa tunggal ogé cairan sareng asesoris khusus. Pasta 2D dikembangkeun khusus pikeun finalisasi éstétika dasar tina restorasi keramik, didamel tina litium disilicate sareng 3D Pro Multilayer. Sadaya bagian tina set oge sadia individual.
DIAJAR DEUI -
KeramikStar® Glaze / Noda Blossom Set
Éta ngandung 17 massa tunggal ogé cairan khusus sareng asesoris. Pasta sareng noda 2D sareng 3D dikembangkeun khusus pikeun finalisasi éstétika profésional pikeun restorasi keramik, didamel tina litium disilicate sareng 3D Pro Multilayer. Sadaya bagian tina set ogé sayogi masing-masing.
DIAJAR DEUI
Multilayer Zirconia Technical Specifications
| Spesifikasi téknis | |||
|---|---|---|---|
| UTML | ST-Plus ML |
STML | |
| ZrO2+ HfO2+Y2O3 | ≥99% | ≥99% | ≥99% |
| Y2O3 | 9% -10% | 7.0% -7.8% | 4.5% -6.0% |
| Al2O3 | ＜ 0.5% | ＜ 0.15% | ＜ 0.5% |
| Density before sintering (g.cm-3) | 3.20 ± 0.05 | 3.15 ± 0.05 | 3.15 ± 0.05 |
| Density after sintering (g.cm-3) | 6.06 ± 0.01 | 6.08 ± 0.01 | 6.09 ± 0.01 |
| CTE (25-500°C) (K-1) | 10.5 ± 0.5 | 10.5 ± 0.5 | 10.5 ± 0.5 |
| Kakuatan lentur saatos sintering (MPa) | > 600 | > 900 | > 1100 |
| Sepuh permukaan eusi fase monoclinic | ＜ 15% | ＜ 15% | ＜ 15% |
| Transmisi cahaya | ＜ 49% | ＜ 46% | ＜ 43% |
| Kalarutan kimiawi saatos sintering (µg.cm-2) | <100 | <100 | <100 |
| Sitotoksisitas | Tingkat 0 | Tingkat 0 | Tingkat 0 |
| Radioaktivitas (Bq.g-1) | <0.1 | <0.1 | <0.1 |
| Suhu sintering (°C) | 1470-1530 | 1480-1530 | 1500-1530 |
| Systems | 98mm / 95mm / 92*75mm | ||
| kakandeleun | 12m / 14mm / 16mm / 18mm / 20mm / 22mm / 25mm | ||
| Bayangan | A1 A2 A3 A3.5 A4 / B1 B2 B3 B4 / C1 C2 C3 C4 / D2 D3 D4 / (ST-Plus ML: BL1 BL2 BL3 BL4) | ||